Zeolite Compositions and Preparation and Use Thereof

ABSTRACT

This invention relates to novel compositions of zeolites or microporous metallosilicates characterised by a continuous spatial distribution of the metal and silicon in the crystals and characterised by a crystal surface enriched in silicon relative to the internal part of the same crystals. This invention also relates to a synthesis method of producing these metallosilicates with spatial distribution of the constituting elements. These novel zeolitic compositions can be used in various hydrocarbon conversion reactions. The crystalline metallosilicates can be selected from the group consisting of aluminosilicates, gallosilicates, ferrosilicates, titanosilicates and borosilicates.

The present invention relates to crystalline metallosilicate, or zeolite, compositions and their preparation and use.

Zeolites have been demonstrated to posses catalytic properties for various types of hydrocarbon conversions. In addition, the zeolites have been used as adsorbents and catalyst carriers for various types of hydrocarbon conversion processes, and other applications. These zeolites are ordered, porous, crystalline material having a definite crystalline structure as determined by x-ray diffraction, possessing a large number of smaller cavities that may be interconnected by pores. The dimensions of these channels or pores are such as to allow adsorption of molecules with certain dimensions while rejecting those with larger dimensions. The interstitial spaces or channels formed by the crystalline network enable zeolites to be used as molecular sieves in separation processes and catalysts and catalyst supports in a wide variety of hydrocarbon conversion processes. Zeolites or metallosilicates are comprised of a lattice of silicon oxide and optionally a metal oxide combined optionally with exchangeable cations such as alkali or alkaline earth metal ions. Although the term “zeolites” includes materials containing silica and optionally alumina, it is recognized that the silica and alumina portions may be replaced in whole or in part with other oxides. For example, germanium oxide can replace the silica portion. The metal cations other than silicon in the oxide framework of metallosilicates may be iron, aluminium, titanium, gallium and boron. Accordingly, the term “Zeolites” means here microporous crystalline metallosilicates materials. The catalytic properties of metallosilicates are the result of the presence of elements different than silicon in the framework of the zeolite. Substitution of metal cations for silicon in the oxide framework gives rise to potential catalytic active sites. The best known metallosilicates are aluminosilicates that exhibit acidic groups in the pores of the crystals. The substitution of silica with elements such as alumina with a lower valence state creates a positive charge deficiency, which can be compensated by a cation such as a hydrogen ion. The acidity of the zeolite can be on the surface of the zeolite and also within the channels of the zeolite. Within a pore of the zeolite, hydrocarbon conversion reactions such as paraffin isomerization, olefin skeletal or double bond isomerization, oligomerisation, disproportionation, alkylation, and transalkylation of aromatics may be governed by constraints imposed by the channel size of the molecular sieve.

The acidic protons, present in the interior of the pores, are subject to shape selective constraints. The principles of “shape selective” catalysis have been extensively reviewed, e.g. by N.Y. Chen, W. E. Garwood and F. G. Dwyer in “Shape selective catalysis in industrial applications”, 36, Marcel Dekker, Inc., 1989. However, acidic groups can also be present at the external surface of the metallosilicate crystals. These acidic groups are not subject to the shape selective constraints imposed by the crystalline pore-structure. The acidic groups on the external surface is called here external surface acidity. The external surface acidity may catalyse undesirable reactions that decrease the product selectivity. Typical unselective surface catalysed reactions that are not subject to the constraints imposed by the crystalline pore-structure are: (1) extensive oligo/polymerisation of olefins, (2) isomerisation of alkylaromatics, selectively produced inside the constrained pore-structure (3) formation of polycyclic aromatics (4) multiple alkylation of aromatics (5) multiple branching of olefins and/or paraffins and (6) formation of macromolecular type precursors of coke leading to undesired carbon laydown. The relative amount of external surface acidity is determined by the crystal size; small crystals posses more external surface acidity than large crystals. It is often advantageous to reduce the presence of the external surface acidity of the zeolites or metallosilicate in order to improve their process performance. Performance measures include product selectivity, product quality and catalyst stability.

Treatment of zeolites to achieve partial dealumination thereby modifying the activity thereof is well known. Conventional techniques for zeolite dealumination include hydrothermal treatment, mineral acid treatment with HCl, HNO3, and H2SO4, and chemical treatment with SiCl4 or ethylenediaminetetraacetic acid (EDTA) or combinations of them. The treatments, however, are not restricted to the zeolite crystal surface. They also modify the internal pores of the zeolites.

Such methods are described for instance in U.S. Pat. No. 3,442,795 and in the articles by Kerr, G. T., in J. Phys. Chem. 71, 4155 (1967) and by Scherzer, J. in J. Catalysis, 54, 285-288 (1978). In these processes, the acid form of a zeolite is subjected to hydrolysis, to remove aluminum from the aluminosilicate framework. The aluminum can then be physically separated to a limited extent from the aluminosilicate by the use of complexing or chelating agents such as ethylenediaminetetraacetic acid or carboxylic acid, to form aluminum complexes that are readily removable from the aluminosilicate. One of the major drawbacks of the prior art dealumination techniques is that they remove aluminium atoms from the entire framework of the zeolite i.e. both the external surface and the internal pores within the zeolite. Whilst removal of the aluminium atoms from the external surface is desirable to moderate non-shape-selective activity of the zeolite, the removal of aluminium atoms from within the pore structure is unwanted because it results hence in a reduction in catalytic sites characterised by their shape-selective constraints in the zeolite pores. Removal of internal aluminium atoms from the framework within the pores can also cause partial destruction of the zeolite pore structure and partial pore blocking due to the presence of amorphous aluminium oxide species.

To minimise the occurrence of undesirable unselective reactions catalysed on the external surface of the zeolite crystals methods have been used to reduce or eliminate surface acidity by extraction with bulky reagents or by surface poisoning. In the prior art various techniques have been employed for preparing external surface deactivated zeolites and hence the relative ratio of internal to external catalysed reactions.

Using larger crystal sizes can increase this ratio. U.S. Pat. No. 4,100,215 describes the use of zeolite crystals greater than 1 micron to increase the para-xylene in the methylation of toluene. However, when diffusion limitation is important, large crystals can reduce the overall catalytic activity.

U.S. Pat. No. 4,001,346 describes a method for preparing a zeolite that has undergone prior treatment to deposit a coating of coke on the surface of the zeolite.

Zeolite modification by treatment with large cations such as cationic nitrogen or phophorus compounds and large branched compounds such as polyamines and the like is described in U.S. Pat. No. 4,101,595. Bulky phenolic and silicating zeolite surface modifying agents are described in U.S. Pat. No. 4,100,215 and U.S. Pat. No. 4,002,697, respectively. The surface acidity of the zeolite can be eliminated or reduced by treatment with bulky dialkylamine reagents as described in U.S. Pat. Nos. 4,520,221 and 4,568,786. U.S. Pat. No. 4,716,135 discloses zeolite catalysts that can be surface inactivated by cofeeding a sterically hindered base organophosphorus compound.

Selective dealumination techniques have been described in the past. U.S. Pat. No. 5,080,878 discloses modifying a crystalline aluminosilicate zeolite with a fluorosilicate salt to extract surface zeolite aluminum, which is replaced by silicon. In accordance with U.S. Pat. No. 5,043,307, the surface acidity of a crystalline aluminosilicate zeolite catalyst is reduced to provide a modified zeolite having enhanced catalytic selectivity for a variety of hydrocarbon conversions and, in particular, for the oligomerization of olefin to provide lubes of high viscosity index. The described process for modifying a crystalline aluminosilicate comprises steaming as synthesized zeolite containing organic template material and then contacting the zeolite in the ammonium, alkali metal, or hydrogen form with a dealuminizing agent which forms a water soluble complex with aluminum. The foregoing treatment results in the reduction of acid sites on the zeolite essentially without affecting its internal structure. As a result, the incidence of undesirable side reactions tending to occur on the surface of the untreated catalyst and which result in lower product yield and/or inferior product characteristics is significantly lessened. Similar processes to prepare surface-inactivated zeolite have been described in U.S. Pat. Nos. 5,234,872, 5,284,989, 5,308,471 and 5,242,676 in which the presence of organics within the zeolite pores facilitates surface dealumination because it precludes the dicarboxylic acid from entering the pores and hence only dealuminating the surface of the zeolite crystals is possible. In another disclosure, U.S. Pat. No. 5,304,695 the use of dealuminating agents, which possesses an average cross section diameter greater than that of the zeolite pores is employed to selective dealuminate the zeolite surface. There is disclosed in U.S. Pat. No. 5,723,710 a new form of zeolite Beta that shows substantially greater stability and greater catalyst lifetime when used in the alkylation and transalkylation of aromatic compounds. This surfacemodified zeolite beta is prepared by treating a templated zeolite Beta with an acid at a pH between about 0 and about 2 and a temperature up to about 125° C. for a time sufficient to modify the chemical environment of the surface aluminum atom without bringing about dealumination of the zeolite beta.

U.S. Pat. No. 4,677,239 and U.S. Pat. No. 4,533,533 describe a process for selective and controlled dealumination of an aluminosilicate zeolite which is achieved by filling the pore system of the zeolite with a foreign material, for example coke, removing part of the foreign material from the outer portion of the zeolite, dealuminating the outer portion, and then removing the remainder of the foreign material and the use of such a partially dealuminated zeolite as catalyst in a toluene disproportionation reaction leads to greater selectivity to paraxylene. These zeolites are characterised as comprising an inner core having silica to alumina ratio substantially characteristic of the untreated zeolite and an outer skin which has higher silica to alumina ratio than said inner core. Other selective surface dealumination processes have been given in U.S. Pat. Nos. 4,654,454 and 4,654,316. The zeolite is ion-exchanged with a first set of cations and than ion-exchanged with a second set of cations which can not enter into the pores of the zeolite and which can be decomposed by thermal treatment. A subsequent dealumination by know techniques results in selective surface dealuminated zeolites.

U.S. Pat. Nos. 4,088,605, 4,148,713 and 4,203,869 disclose a crystalline aluminosilicate zeolite particle containing an aluminum-free outer shell prepared by carrying out the crystallization in a crystallization medium for a given period of time and then altering the crystallization medium to eliminate the aluminum therein. This can be accomplished by a total replacement of the reaction mixture or by complexation of any remaining aluminum ion from the original reaction mixture with reagents such as gluconic acid, tartaric acid, nitrilotriacetic acid or EDTA. These methods, however, often increase the complexity of the process. It is a two-step process. In order to be able to control such processes operating conditions have to be such that the crystallisation reactions are slow enough so as to interrupt at the right moment the crystallisation process and alter the reaction medium. Moreover, the organic complexing compounds do not resist the high reaction temperature needed to produce zeolites in an economic viable period of time. Zeolite type catalyst having a double structure that comprises a core made of crystalline borosilicate and a shell made of crystalline silicon oxide has been described in U.S. Pat. No. 4,503,164. In U.S. Pat. No. 4,788,374 a surfaceinactive shape selective metallosilicate catalyst, useful for the conversion of lower molecular weight olefins to liquid hydrocarbons such as gasoline, distillate, and high viscosity lube oils, is prepared by a process comprising forming a silica shell on a metallosilicate core by crystallizing silica in the presence of fluoride ion onto the surface of the core. The catalyst prepared according to the process of the mentioned invention comprises an inner portion and an outer portion disposed as a porous shell around the inner portion wherein the inner portion comprises a medium pore metallosilicate and the outer portion comprises crystalline silica substantially free of acid sites, the outer portion being crystallised from an alkaline silicate solution containing fluoride ion. In U.S. Pat. No. 6,013,851 a catalyst having a core and surface layer, providing a lower branching in olefin oligomerisation has been described. Each particle of the molecular sieve comprising a core having deposited thereon a surface layer, the core comprising a zeolite containing silicon and aluminium, and the surface layer comprising a zeolite containing silicon and aluminium, the zeolite of the surface layer being of the same crystalline structure as the core and having a higher silicon:aluminium ratio than that of the core. U.S. Pat. No. 5,994,603 discloses the use of a zeolite bound zeolite for methylation of toluene to para-xylene. Prior to using in commercial processes, the zeolite crystals are usually bound. When such a bound zeolite is used in catalytic conversion processes such as toluene methylation, the binder may affect the chemical reactions that are taking place within the zeolite and also may it catalyse undesirable reactions that can result in the formation of undesirable products. The use of second zeolite crystals as a binder results in a catalyst which provides a means for controlling undesirable reactions taking place on or near the surface of the first zeolite crystals since the acidity of the second zeolite can be carefully controlled and can have improved mass transfer of reactants and greater access to and from the pores of the zeolite. The zeolite bound zeolite catalyst used in the process of the described invention is preferably prepared by a three-step procedure. The first step involves the synthesis of the first zeolite crystals. Next, a silica-bound aluminosilicate zeolite is prepared preferably by mixing a mixture comprising the aluminosilicate zeolite crystals, a silica gel or sol, water and optionally an extrusion aid and, optionally, the metal component until a homogeneous composition in the form of an extrudable paste develops. The final step in the three step catalyst preparation process is the conversion of the silica present in the silica-bound catalyst to a second zeolite which serves to bind the first zeolite crystals together. The first zeolite crystals are thus held together without the use of a significant amount of non-zeolite binder. To prepare the zeolite bound zeolite catalyst, the silica-bound aggregate can be first aged in an appropriate aqueous solution at an elevated temperature. Next, the contents of the solution and the temperature at which the aggregate is aged should be selected to convert the amorphous silica binder into the second zeolite. It is preferable that the second zeolite be of the same type as the first zeolite.

Several processes have been described for coating of the external surface of zeolite crystals with a silica layer by means of vapour phase or liquid phase deposition techniques of organosilicon compounds (U.S. Pat. Nos. 4,465,886, 4,477,583, 4,950,835, 5,349,113, 5,349,114, 5,365,004, 5,365,003, 5,403,800 and 5,659,098). These preparation methods use expensive silicon compounds and require often several steps, making the process difficult to reproduce. Deposition of silicon coating is not always limited to the external surface and the internal surface may also be inactivated resulting in a significant reduced catalytic activity.

The above described processes for preparing zeolites with reduced surface activity and hence increased product selectivity are all multi-step processes requiring post-treatment steps after the initial synthesis of the zeolite having still significant surface activity. There is thus a need for an improved method to prepare more efficiently zeolites with reduced surface activity. In has never been recognised how to prepare in a controlled manner in a one-step process zeolites or metallosilicates characterised directly by a spatial distribution of the constituting elements and hence a strongly reduced surface activity without requiring post-treatment steps.

Classical zeolite or metallosilicates syntheses are carried out in aqueous media under hydrothermal and autogeneous conditions. The aqueous solution contains the nutrients as the metal precursor compound, the silicon precursor, mineralisers and often also organic compound that act as template or as pore fillers during the crystallisation process. A typical preparation involves heating a mixture, containing a source of silica and optionally a source of a second metal, like aluminium, iron, gallium, boron and titanium, in water in the presence of a mineralizer and a template or a structure-directing agent until crystallisation occurs. The general principles of zeolite synthesis are well documented, e.g. “Synthesis of High-silica Aluminosilicate Zeolites”, Study of Surface Science and Catalysis, vol. 33, Elsevier, 1987 and “Synthesis of Aluminosilicate Zeolites and Related Silica-based Materials”, Catalysis and Zeolites: Fundamentals and Applications, Springer, 1999. The mineralizers who are usually alkali or alkaline earth hydroxides, provide the function of a solubilizer of the silicon and second metal sources transporting them through the reaction solution or gel to nucleation sites or growing crystals. The template can be a cationic or a neutral organic compound and tends to favour the formation of a particular zeolite structure. The templates and mineralisers may further control the pH of the medium and may provide charge balance with the anionic framework of the metallosilicate. Various organic molecules have been described in the prior art, which have different kinds of functions beside pore-filler effects. These additional organic molecules may favour the formation of a particular zeolite structure above another one.

U.S. Pat. No. 5,063,038 and U.S. Pat. No. 5,160,500 provide methods for preparing a zeolite other than ZSM-5 from a reaction mixture comprising a mixed organic directing agent which is a combination of (a) an organic nitrogen containing compound such as an amine or a quaternary ammonium compound and (b) an alcohol and/or diol. Particular zeolites synthesized by this method include ZSM-22 and ZSM-23. The use of an alcohol or a diol inhibits the coformation of ZSM-5. Especially when used to prepare ZSM-23, this method enables the preparation of more catalytically active ZSM-23 of reduced crystallite size and also enables the use of lower crystallisation temperatures. U.S. Pat. No. 4,199,556 discloses the use of alcohols with 2 to 5 carbons together with seeds of the ZSM-5 crystals and ammonium hydroxide to obtain products substantially deficient of organic ammonium cations. U.S. Pat. No. 3,702,886 describes the synthesis of ZSM-5 in the presence of glycerol leading to elongated crystals. EP-A-87017 discloses a process for the production of new zeolite structure by reacting an aqueous mixture containing a silica source, an alumina source, an alkali or alkaline earth source and methanol. In EP-A-102497 the use of ethylene glycol is described for the preparation of crystalline silicates. Ethylene glycol does not remain in the crystalline silicates, but plays the role in the formation of the desired crystalline structure. In the above given disclosures the additional organic compounds are water-soluble and play the role of structure-directing agent. Jacobs et al. reviewed the synthesis of ZSM-5 in the presence of alcohols in “Synthesis of High-Silica Aluminosilicate Zeolites”, Study of Surface Science and Catalysis, vol. 33, Elsevier, 1987. Various water-soluble alcohols have different effects on crystallisation efficiency and crystal size.

Bibby et al. in Nature, 317, p. 157, 1985 discloses the preparation of sodalite in a non-aqueous solvent system, exemplified by ethylene glycol or propanol. Erp et al. in Zeolites, 7, p. 286, 1987 and Qisheng et al. in J. Chem. Soc., Chem. Commun., p. 1486, 1988 describe the synthesis of zeolites with 4, 5 or 6 membered rings in organic solvents, including glycols, glycerol, sulfolane, dimethylsulfoxide, ethanol, pyridine and C₆-C₇ alcohols. In U.S. Pat. No. 5,320,822 a process is described for the synthesis of large crystals of the order of 0.3-3 mm in size. The zeolites are prepared in a growth medium containing the silica, alumina and charge balancing ion sources, a nitrogen-containing organic base, hydrogen fluoride and optionally an organic solvent and water in an amount such that the ratio water to framework atoms is no greater than about 6 molar and such that the ratio of water to nitrogen-containing base is no greater than 0.3 molar. The examples given above show that certain zeolites can be synthesised in essential water-free organic solvent media, given rise to particular zeolite structures or zeolite crystal textures.

The prior art provides processes in which a primary prepared zeolite is post-treated to coat the primary prepared zeolite in a second step with a shell of secondary prepared zeolite or to coat the primary prepared zeolite in a second step with a layer of silica with the aim to provide zeolite particles in which the composition of the core is different from the composition of the shell of the particles.

Therefore, it is an aim of the present invention to provide novel zeolite or metallosilicate compositions prepared by direct one-step synthesis characterised by a continuous spatial distribution of the constituting elements and characterised by a crystal outer surface enriched in silicon relative to the inner part of the same crystals. As a result, the metallosilicates with novel compositions characterised by a spatial distribution of the constituting elements have reduced surface activity relative to the internal pores, which are subject to shape-selective constraints of the pore-structure. Such a continuous spatial distribution permits to avoid problems of lack of selectivity observed for some reactions performed with compositions without continuous spatial distribution. It is a further aim of the present invention to provide a process for preparing in a controlled manner in a one-step process metallosilicates characterised with a continuous spatial distribution of the constituting elements, not requiring any additional post-treatment step.

The present invention provides process for producing a crystalline metallosilicate composition, the method comprising the steps of: —

a. providing an aqueous liquid phase comprising at least one silicon-containing compound and at least one metal-containing compound; and b. crystallising the crystalline metallosilicate composition from the aqueous liquid phase, the crystallising step having a first stage followed by a second stage and wherein the concentration of the at least one silicon-containing compound in the aqueous liquid phase is increased in the second stage.

Preferably, in the second stage the concentration of the at least one silicon-containing compound in the aqueous liquid phase is increased by removing water from the aqueous liquid phase.

More preferably, the crystallising step is carried out in a closed reaction vessel under elevated temperature and water is removed by permitting steam to be released from the reaction vessel.

Preferably, the elevated temperature is from 80 to 250° C.

The steam may be progressively released over the second stage. Alternatively, the steam is released at the commencement of the second stage.

Preferably, at the commencement of the second stage the molar ratio of water to the at least one silicon-containing compound is from 60 to 15, more preferably from 45 to 20.

Preferably, at the termination of the second stage the molar ratio of water to the at least one silicon-containing compound is from 54 to 7.5, more preferably from 30 to 12.

Preferably, during the second stage the molar ratio of water to the at least one silicon-containing compound decreases by from 10 to 75%, more preferably from 20 to 50%.

Preferably, the at least one silicon-containing compound is selected from at least one of an alkali metal silicate, a tetraalkyl orthosilicate, precipitated silica, pyrogenic silica, and an aqueous colloidal suspension of silica.

Preferably, the at least one metal-containing compound is selected from at least one of the metal oxide, a metal salt, and a metal alkoxide.

Preferably, the metallosilicate is an aluminosilicate, and the at least one metal-containing compound comprises an aluminium compound for which the source of aluminum is selected from at least one of hydrated alumina dissolved in an alkaline solution, aluminum metal, a water-soluble aluminum salt, such as aluminum sulphate or aluminium chloride, sodium aluminate and an alkoxide, such as aluminum isopropoxide

Preferably, the metallosilicate is a borosilicate, and the at least one metal-containing compound comprises a boron compound for which the source of boron is selected from at least one of hydrated boron oxide dissolved in an alkaline solution, a water-soluble boron salt, such as boron chloride, and an alkoxide.

Preferably, the metallosilicate is a ferrosilicate, and, the at least one metal-containing compound comprises an iron compound for which the source of iron is a water soluble iron salt.

Preferably, the metallosilicate is a gallosilicate, and the at least one metal-containing compound comprises a gallium compound for which the source of gallium is a water soluble gallium salt.

Preferably, the metallosilicate is a titanosilicate, and the at least one metal-containing compound comprises a titanium compound for which the source of titanium is selected from at least one of titanium halides, titanium oxyhalides, titanium sulphates and titanium alkoxides.

The present invention also provides a process for producing a crystalline metallosilicate composition, the method comprising the steps of: —

(a) providing an aqueous liquid comprising at least one silicon-containing compound dissolved or dispersed therein and at least one metal-containing compound dissolved or dispersed therein; (b) crystallising the crystalline metallosilicate composition from the aqueous liquid medium in a vessel under autogenous conditions, wherein in at least an end phase of the crystallising step a portion of the water is removed from the vessel; and (c) isolating the crystallised product.

Thus in step (b), autogeneous conditions are maintained until at least the end phase wherein the water is removed from the vessel.

Preferably, the water is removed as vapour.

Preferably, the water removal causes the concentration of at least the at least one silicon-containing compound dissolved or dispersed in the aqueous liquid to be increased.

The present invention further provides a crystalline metallosilicate composition comprising crystallites having a crystal outer surface layer having a depth of about 10 nm below the outer surface, and an inner part extending inwardly from a depth of about 50 nm below the outer surface, wherein the atomic ratio of silicon to metal in the metallosilicate composition is at least 1.75 times higher in the crystal outer surface layer as compared to that in the inner part.

The crystalline metallosilicate composition comprising crystallites provided by the invention is characterised by a continuous spatial distribution of the silicon to metal, and has an atomic ratio of silicon to metal in the metallosicilate composition which decreases continuously from the outer surface to the inner part of the crystal.

Preferably, the inner part has a silicon/metal atomic ratio of from 15 to 1000, more preferably from 20 to 500, and the crystal surface has a silicon/metal atomic ratio of from 22.5 to 15000, more preferably from 45 to 5000.

Preferably, the inner part has a substantially constant silicon/metal atomic ratio.

Preferably, in the inner part the silicon/metal atomic ratio in the walls, constituting the pores in the crystalline metallosilicate composition, is substantially the same as the average silicon/metal atomic ratio of the inner part.

Preferably, the metallosilicate is an aluminosilicate, a borosilicate, a ferrosilicate, a gallosilicate, or a titanosilicate

The present invention additionally provides the use of the crystalline metallosilicate composition of the invention as a catalyst component in a hydrocarbon conversion process.

To the inventors' knowledge it has never previously been recognised that the change of the concentration of the aqueous medium during the crystallisation process could result in continuous spatial distribution of the constituting elements and could result a crystal surface of the metallosilicate that is enriched in silicon compared to the inner part of the same crystals. The present invention provides a method for preparing in a one-step process metallosilicate crystals characterised by a continuous spatial distribution of the constituting elements and characterised by a surface composition that is enriched in silicon compared to the inner part of the same crystals by using a two-stage crystallisation step where the concentration of the silicon-containing component(s) in the crystallisation medium is changed during the crystallisation step, and in particular is increased at a latter stage of the crystallisation step, for example by removal of water from the reaction conditions.

The process of the present invention for preparing metallosilicates with novel compositions characterised by a continuous spatial distribution of the constituting elements and characterised by a surface enriched in silicon preferably comprises the following procedure:

-   1. preparing an aqueous reaction mixture containing sources of a     trivalent metal oxide such as aluminium oxide, iron oxide, boron     oxide or gallium oxide, tetravalent oxides such as silica, germania     and titania, alkali metal or ammonium cations and optionally a     structure-directing agent; -   2. heating the aqueous mixture optionally under agitation and for     sufficient time at a sufficient temperature to achieve     crystallisation of the desired metallosilicate; -   3. concentrating the aqueous mixture by vaporising part of the water     contained in the aqueous mixture during sufficient time; and -   4. stopping the crystallisation process by cooling the     crystallisation mixture, filtering and washing the crystals to     remove any non-crystallised nutrients.

Embodiments of the present invention will now be described by way of example only with reference to the accompanying drawings, in which: —

FIG. 1 is a graph which shows the relationship between Si/Al atomic ratio and sputtering depth for crystalline metallosilicates produced in accordance with Comparative Example 1;

FIG. 2 is a graph which shows the relationship between Si/Al atomic ratio and sputtering depth for crystalline metallosilicates produced in accordance with Comparative Example 2;

FIG. 3 is a graph which shows the relationship between Si/Al atomic ratio and sputtering depth for crystalline metallosilicates produced in accordance with Example 1 of the invention;

Metallosilicates characterised by a spatial distribution of the constituting elements and characterised by a surface enriched in silicon that can be produced by the process of the present invention can be any of the synthetic crystalline zeolites. Examples of these zeolites include large pore zeolites, medium pore size zeolites, and small pore zeolites. These zeolites and their isotypes are described in “Atlas of Zeolite Structure Types”, eds. W. H. Meier, D. H. Olson and Ch. Baerlocher, Elsevier, Fourth Edition, 1996, which is hereby incorporated by reference. The structure types are provided by the “IUPAC Commission of Zeolite Nomenclature”. A large pore zeolite has a pore size of at least about 0.7 nm and includes the following structure types with examples given between brackets: LTL (L), MAZ (mazzite, Omega, ZSM-4), MEI (ZSM-18), FAU (zeolite Y, zeolite X), EMT (CSZ-1, ECR-30, ZSM-3 and ZSM-20), OFF (Offretite), *BEA (Beta), MWW (MCM-22, ITQ-1, PSH-3, SSZ-25, ERB-1) and MOR (Mordenite). A medium pore size zeolite generally has a pore size from about 0.5 nm to about 0.7 nm and includes, for example, CON (CIT-1, SSZ-26, SSZ-33), IFR (ITQ-4, MCM-58 and SSZ-42), MFI (ZSM-5, silicalite, TS-1), MEL (ZSM-11, silicalite-2, TS-2), MTW (ZSM-12, CSH-5, Nu-13, Theta-3), EUO (ZSM-50, TPZ-3), MTT (ZSM-23, EU-13, ISI-4, KZ-1), MFS (ZSM-57), HEU (Clinoptilolite), FER (ZSM35, Ferrierite, FU-9, ISI-6, NU-23, Sr-D), NES (NU-87), SFF (SSZ-44), STF (SSZ-35) and TON (ZSM-22, Theta-1, ISI-1, KZ-2 and NU-10) structure types. A small pore size zeolite has a pore size from about 0.3 nm to about 0.5 nm and includes, for example, CHA (Chabasite), ERI (Erionite).

In general, the chemical formula of anhydrous crystalline metallosilicate expressed in terms of moles may be represented by the formula:

(4-n)/mM.(TO2). SiO2)x

Wherein “M” is selected from the group consisting of hydrogen, ammonium, monovalent, divalent and trivalent cations and mixtures thereof; “m” is the valence of the charge-balancing cation “M” and “x” is a number of at least 2, preferably at least 10, said value being dependent upon the particular type of zeolite, and “T” is a metal in the anionic oxide framework structure of the metallosilicate such as aluminium, gallium, boron, iron, or titanium. n″ the valence of the “T”. “2x” is also the molar ratio of silica to “T” metaloxide. “x” is the atom/atom ratio of silicon to “T” metal in the framework of the metallosilicate.

The sources of the various elements of the metallosilicate may be any of those find in the commerce or prepared on purpose. For example, the source of silicon may be a silicate, e.g., an alkali metal silicate, a tetraalkyl orthosilicate, precipitated or pyrogenic silica, or preferably an aqueous colloidal suspension of silica. When the metallosilicate is an aluminosilicate zeolite, the source of aluminum is preferably hydrated alumina dissolved in an alkaline solution or aluminum metal, a water-soluble aluminum salt, e.g., aluminum sulphate or aluminium chloride, sodium-aluminate or an alkoxide, e.g., aluminum isopropoxide. When the metallosilicate is a borosilicate zeolite, the source of boron is preferably hydrated boron oxide dissolved in an alkaline solution or a water-soluble boron salt, e.g., boron chloride or an alkoxide. When the metallosilicate is a ferrosilicate or gallosilicate, the source of iron or gallium can almost be any iron or gallium salts that is readily soluble in water. When the metallosilicate is titanosilicate, the source of titanium can be titanium halides, titanium oxyhalides, titanium sulphates or titanium alkoxides. The atom/atom ratio of silicon to metal “T” depends on the metal “T” and on the application of the metallosilicate and is at least 2/1 to about 10000/1, preferably from 5/1 to about 5000/1 and most preferred from about 10/1 to 1000/1. In the aqueous crystallisation medium the amount of potential metallosilicate, based on the anhydrous formula given above can be from about 1 to about 50 weight percent, preferably from 4 to 25 and most preferred from 6 to 15 weight percent. Optionally one or more directing agents, such as organic or inorganic compounds containing nitrogen, oxygen, sulfur, or phosphorous may be introduced into the synthesis mixture. When the directing agent is a cation, it may also be introduced in the form of a mixture of hydroxide and salt, e.g., a halide. The agent used will depend on the metallosilicate prepared by the process. The amount of the directing agent depends on the metallosilicate prepared by the process. The source of “M” cations may be alkali or alkaline earth hydroxides or salts. “M” may also be ammonium hydroxide or salts. Together with the directing agent(s) the “M” cation will determine the pH of the crystallising medium. The pH is generally between 8 and 13. Its starting value will be depended on the metallosilicate prepared by the process and by the desired size of the crystals and desired rate at which the crystallisation has to proceed.

The term “near” the surface of the metallosilicate crystals means here the outer region of the crystals with a depth of up to about 10 nm. The atom/atom ratio of silicon to metal “M” near the surface of the crystals prepared according to the present invention is at least 1.5 times higher than the overall bulk silicon to metal “M” ratio, preferably from 1.5 to 15, more preferably from 2 to 10, most preferably from 3 to 5 times higher than the bulk composition, which extends inwardly from a depth of 50 nm or greater.

The order of mixing of the ingredients is not essential and will depend largely on the zeolite being prepared. For instance, two or more separate mixtures, can be prepared each containing one or more of the constituting elements. First the aqueous mixtures can be mixed in a controlled manner under vigorous stirring. Generally a homogeneous gel or sol is produced upon the mixing of the aqueous mixtures. This crystallisation medium precursor may be aged at a temperature at which no crystallisation occurs, optionally nucleation may be started. Persons skilled in the art know equipment used to prepare the zeolite crystals of the present invention. Generally, metallosilicates can be prepared by using autoclaves, which have sufficient agitation to homogenise the crystallisation mixture during heat up until the effective nucleation and crystallisation temperature of the mixture is achieved. The crystallisation vessel can be made of a metal or metal alloys resisting the conditions of the crystallisation or optionally can be coated with a fluorocarbon such as Teflon®™. Other means of introducing agitation known to one skilled in the art can be employed, such as pumping the synthesis mixture from one part of the autoclave to another or using special agitation devices like Archimedes type screw for gentle agitating. Once the crystallisation temperature is reached, the agitation can be continued or can be stopped. Generally the agitation of the aqueous medium is fairly gentle; preferably the rotation speed of a blade-type agitator is not higher than about 250 rpm.

During crystallising of the crystalline metallosilicate composition from the aqueous liquid phase, the crystallising step has a first stage followed by a second stage and wherein the concentration of the at least one silicon-containing compound in the aqueous liquid phase is increased in the second stage. In the second stage the concentration of the at least one silicon-containing compound in the aqueous liquid phase is increased by removing water from the aqueous liquid phase. The crystallising step is carried out in a closed reaction vessel under elevated temperature and water is removed by permitting steam to be released from the reaction vessel. Therefore the crystallising of the crystalline metallosilicate composition from the aqueous liquid medium is carried out in a vessel under autogenous conditions, wherein in at least an end phase of the crystallising step a portion of the water is removed from the vessel. After the crystallisation step has been terminated, the crystallised product is isolated.

At the start of the crystallisation step, the synthesis mixture typically has an initial H2O/SiO2 molar ratio from 60 to 15, more preferably from 45 to 20. At the end phase of the crystallising step there is a concentration step of the at least one silicon-containing compound in such a way that the resulting H2O/SiO2 molar ratio is lowered by a proportion, compared to the original molar ratio, of typically from 10% to 75%, more preferably from 20% to 50%. (this result in (i) starting from 60 in 54-15, preferably 48-30 and (ii) starting from 15 in 13.5-3.75, preferably 12-7.5)

It is known by the persons skilled in the art that the time needed to crystallise a metallosilicate depends to some extent on the chemical composition of the synthesis mixture but also on the temperature. The synthesis of these kind of zeolites can be done from about 80° C. up to 250° C. for a time ranging from 1 hour up to 2 weeks. In general the lower the synthesis temperature, the longer the crystallisation time needed.

The concentration steps can be done in from 0.5 hours up to 24 hours, preferably from 1 hours up to 12 hours and most preferably from 2 to 8 hours. The concentration step can be done progressively over the second stage of the crystallisation step, or only initially at the commencement of the second stage of the crystallisation step.

Upon completion of crystallization of the metallosilicate, the product crystals are separated from the reaction mixture by, for example, cooling and filtering, and water washed and dried at a temperature of typically from about 25° C. to about 250° C., and more preferably from 80° C. to about 120° C. The crystals prepared by the instant invention can be formed into a wide variety of forms. In cases where a catalyst is produced from the metallosilicate produced by the present invention, the catalyst needs to possess a shape to be applicable in industrial reactors. The crystals can be shaped before drying or partially dried and then shaped or the crystals can be calcined to remove organic template and then shaped. In the case of many catalysts, it is desirable that crystalline zeolites prepared by the process of the present invention are incorporated with binder material resistant to the temperature and other conditions employed in organic conversion processes. It will be easily understood by the person skilled in the art that binder material does not contain the metal element “T” that is incorporated into the framework of the metallosilicate characterised by a spatial distribution of the constituting elements and characterised by a surface enriched in silicon. In addition, the binder material does not contain elements that destroy the spatial distribution of the constituting elements of the metallosilicate or the surface enriched in silicon of the metallosilicate. Examples of binder material may be composited with a porous matrix material, such as silica, zirconia, magnesia, titania, silica-magnesia, silica-zirconia, silica-thoria, and silica-titania, as well as ternary compositions, such as silica-magnesia-zirconia. The relative proportions of metallosilicate component and binder material will vary widely with the metallosilicate content ranging from between about 1 to about 99 percent by weight, more preferably in the range of about 10 to about 85 percent by weight of metallosilicate component, and still more preferred from about 20 to about 80 percent. The metallosilicate prepared by the process of the present invention may be further ion exchanged after calcination to remove organic template as is known in the art either to replace at least in part the original charge-balancing cations present in the metallosilicate with a different cation, e.g. a Group IB to VIII of the Periodic Table metal such as tungsten, molybdenum, nickel, copper, zinc, palladium, platinum, calcium or rare earth metal, or to provide a more acidic form of the zeolite by exchange of original charge-balancing cation with ammonium cations, followed by calcination of the ammonium form to provide the acidic hydrogen form. The acidic form may be readily prepared by ion exchange using a suitable reagent such as ammonium nitrate, ammonium carbonate or protonic acids, like HCl, HNO3 and H3PO4. The metallosilicate may then be calcined at a temperature of 400 to 5500° C. to remove ammonia and create the hydrogen form. Particularly preferred cations will depend on the use of the metallosilicate and include hydrogen, rare earth metals, and metals of Groups IIA, 1 IIA, IVA, IB, IIB, IIIB, IVB, and VIII of the Periodic Table of the Elements. The metallosilicate prepared by the process of the present invention may be further supported by at least one different precursor of metals that have catalytic activity after known pretreatments, e.g. a Group IIA, IIIA to VIIIA, IB, IIB, IIIB to VIB of the Periodic Table metal such as tungsten, molybdenum, nickel, copper, zinc, palladium, platinum, gallium, tin, and/or tellurium metal precursors.

Since the metallosilicate of the present invention characterised by a spatial distribution of the constituted elements and characterised by a surface enriched in silicon have controlled catalytic activity which is the results of the presence of catalytic active sites mainly in the inner part of the metallosilicate crystals and largely the absence of unselective catalytic active sites near the external surface of the metallosilicate crystals, which can cause undesirable side reactions to occur, the metallosilicate of the present invention by itself or in combination with one or more catalytically active substances can have high activity, high selectivity, high stability, or combinations thereof when used as catalysts for a variety of hydrocarbon conversion processes. Examples of such processes include, as non-limiting examples, the following:

-   1. The alkylation of aromatic hydrocarbons with light olefins to     provide short chain alkyl aromatic compounds, e.g., the alkylation     of benzene with propylene to provide cumene and alkylation of     benzene with ethylene to provide ethylbenzene. Typical reaction     conditions include a temperature of from about 100° C. to about 450°     C., a pressure of from about 5 to about 80 bars, and an aromatic     hydrocarbon weight hourly space velocity of from 1 hr1 to about 100     hr⁻¹. -   2. The alkylation of polycyclic aromatic hydrocarbons with light     olefins to provide short chain alkyl polycyclic aromatic compounds,     e.g., the alkylation of naphthalene with propylene to provide mono-     or di-isopropyl-naphthalene. Typical reaction conditions include a     temperature of from about 100° C. to about 400° C., a pressure of     from about 2 to about 80 bars, and an aromatic hydrocarbon weight     hourly space velocity of from 1 hr⁻¹ to about 100 hr⁻¹ -   3. The alkylation of aromatic hydrocarbons, e.g., benzene and     alkylbenzenes, in the presence of an alkylating agent, e.g., alkyl     halides and alcohols having 1 to about 20 carbon atoms. Typical     reaction conditions include a temperature of from about 100° C. to     about 550° C., a pressure of from about atmospheric to about 50     bars, a weight hourly space velocity of from about 1 hr⁻¹ to about     1000 hr⁻¹ and an aromatic hydrocarbon/alkylating agent mole ratio of     from about 1/1 to about 20/1. -   4. The alkylation of aromatic hydrocarbons, e.g., benzene, with long     chain olefins, e.g., C14 olefin. Typical reaction conditions include     a temperature of from about 50° C. to about 300° C., a pressure of     from about atmospheric to about 200 bars, a weight hourly space     velocity of from about 2 hr⁻¹ to about 1000 hr⁻¹ and an aromatic     hydrocarbon/olefin mole ratio of from about 1/1 to about 20/1. -   5. The alkylation of phenols with olefins or equivalent alcohols to     provide long chain alkyl phenols. Typical reaction conditions     include temperatures from about 100° C. to about 250° C., pressures     from about 1 to 50 bars and total weight hourly space velocity of     from about 2 hr⁻¹ to about 10 hr⁻¹. -   6. The transalkylation of aromatic hydrocarbons in the presence of     polyalkylaromatic hydrocarbons. Typical reaction conditions include     a temperature of from about 150° C. to about 550° C., a pressure of     from about atmospheric to about 100 bars, a weight hourly space     velocity of from about 1 to about 500 hr⁻¹ and an aromatic     hydrocarbon/polyalkylaromatic hydrocarbon mole ratio of from about     1/1 to about 20/1. -   7. The isomerization of aromatic (e.g., xylene) feedstock     components. Typical reaction conditions for such include a     temperature of from about 200° C. to about 550° C., a pressure of     from about 1 bars to about 50 bars, a weight hourly space velocity     of from about 0.1 to about 200 hr⁻¹ and a hydrogen/hydrocarbon mole     ratio of from about 0 to about 100. -   8. The disproportionation of toluene to make benzene and paraxylene.     Typical reaction conditions including a temperature of from about     200° C. to about 600° C., a pressure of from about atmospheric to     about 60 bar, and a weight hourly space velocity of from about 0.1     hr⁻¹ to about 30 hr⁻¹. -   9. The catalytic cracking of naphtha feed to produce light olefins.     Typical reaction conditions include from about 450° C. to about 650°     C., pressures of atmospheric to about 8 bars and weight hourly space     velocity of from about 5 to 50 hr⁻¹. -   10. The catalytic cracking of butenes feed to produce light olefins,     e.g. propylene. Typical reaction conditions include from about     450° C. to about 650° C., pressures of atmospheric to about 8 bars     and weight hourly space velocity of from about 5 to 50 hr⁻¹. -   11. The catalytic cracking of high molecular weight hydrocarbons to     lower weight hydrocarbons. The metallosilicate of the instant     invention may be employed in combination with conventional catalyst     used in fluid catalytic cracking units. Typical reaction conditions     for catalytic cracking include temperatures of from about 450° C. to     about 650° C., pressures of from about 0.1 bar to about 10 bars, and     weight hourly space velocities of from about 1 to about 300 hr⁻¹. -   12. The dewaxing of hydrocarbons by selectively removing straight     chain paraffins. Typical reaction conditions include a temperature     between about 200° C. and 450° C., a pressure from 10 to up to 100     bars and a liquid hourly space velocity from 0.1 to 20 hr⁻¹. -   13. The hydrocracking of heavy petroleum feedstocks. The     metallosilicate catalyst contains an effective amount of at least     one hydrogenation component of the type employed in hydrocracking     catalysts. -   14. A combination hydrocracking/dewaxing process in which optionally     more than one metallosilicate or combinations of metallosilicate     with other zeolites or molecular sieves are employed. -   15. The conversion of light paraffins to olefins and/or aromatics.     Typical reaction conditions include temperatures from about 425° C.     to about 750° C. and pressures from about 1 to about 60 bars. -   16. The conversion of light olefins to gasoline, distillate and lube     range hydrocarbons. Typical reaction conditions include temperatures     of from about 175° C. to about 450° C. and a pressure of from about     3 to about 100 bars. -   17. The conversion of naphtha (e.g. C6-C10) into products having a     substantial higher octane aromatics content by contacting the     hydrocarbon feed with the catalyst at a temperature in the range of     from about 400° C. to 600° C., preferably 480° C. to 5500° C. at     pressures ranging from atmospheric to 40 bar and liquid hourly space     velocities ranging from 0.1 to 35 hr⁻¹. -   18. The reaction of alcohols with olefins to provide mixed ethers,     e.g., the reaction of methanol or ethanol with isobutene and/or     isopentene to provide methyl-t-butyl ether (MTBE) or ethyl-t-butyl     ether (ETBE) and/or t-amyl methyl ether (TAME) or t-amyl-ethyl-ether     (TAEE). Typical conversion conditions including temperatures from     about 20° C. to about 250° C., pressures from 2 to about 100 bar, a     liquid hourly space from about 0.1 hr⁻¹ to about 200 hr⁻¹ and an     alcohol to olefin molar feed ratio from about 0.2/1 to about 3/1. -   19. The decomposition of ethers like MTBE, ETBE, TAME or TAEE into     isobutene and isopentenes and the corresponding alcohol. Typical     conversion conditions including temperatures from about 20° C. to     about 300° C., pressures from 0.5 to about 10 bars, a liquid hourly     space from about 0.1 hr⁻¹ to about 200 hr⁻¹. -   20. The conversion of oxygenates, e.g., alcohols, such as methanol,     or ethers, such as dimethylether, or mixtures thereof to     hydrocarbons including olefins and aromatics with reaction     conditions including a temperature of from about 275° C. to about     600° C., a pressure of from about 0.5 bar to about 60 bar and a     liquid hourly space velocity of from about 0.1 to about 100 hr⁻¹ -   21. The oligomerization of straight and branched chain olefins     having from about 2 to about 10 carbon atoms. The oligomers that are     the products of the process have 6 to about 50 carbons, which are     useful for both fuels blending feedstock, as solvents, lube oils,     alkylation agents and reactants for preparing various kinds of     oxygen containing chemicals. The oligomerization process is     generally carried out at a temperature in the range of from about     150° C. to about 350° C., a liquid hourly space velocity of from     about 0.2 to about 70 hr⁻¹ and a pressure of from about 5 to about     100 bar.

The invention is illustrated by the following non-limiting Examples.

In the following Examples, the techniques used to produce and characterise the obtained materials are given.

X-ray diffraction was used to obtain a diffraction pattern, to ensure that desired crystal structure is confirmed or to detect presence of foreign crystalline phases and to determine degree of crystallinity compared with a reference zeolite. The diffractometer was a Philips PW1830 (Co Kα). To determine percentage of zeolite crystallinity, the intensity of 7 peaks (15.5, 16.25, 17.2, 18, 18.5, 27, 28 °2θ) typical for MFI zeolites was normalised to those of the reference zeolite.

The spatial distribution of the constituting elements was measured by means of “secondary ion mass spectrometry” or SIMS. The apparatus used was a CAMECA TOF-SIMS IV. To avoid charge effects, zeolites being non-conductive materials, a low energy electron floodgun was used. To realise in depth composition profiles, a sputtering gun was used simultaneously to the analysis gun. Both guns used argon as primary ions, the energy of the sputtering gun ion beam being 3 keV for a current density of 20 nA, and the analysis gun having an energy of 10 keV with a current of 1 pA.

The sputtering gun eroded a surface area of 200×200 micron, and the surface analysis gun scanned a surface area of about 5×5 micron. Profiles were performed in non-interlaced mode, meaning that analysis and sputtering of the samples was completely dissociated. The cycle sequence was as follows: 30 seconds analysis−30 seconds sputtering−2 seconds pausing. Zeolite powder was compacted and pressed into a wafer. The wafers were fixed on a support and placed in a vacuum of 10-6 to 10-7 Torr. After degassing for a period of 24 hours analysis was performed. Only monoatomic species of aluminium and silicon were taken into account for concentration profiles and only the double charged cations are considered for quantitative measurements (Si²⁺/Al²⁺). A prior calibration had been realised on zeolites with well know Si/AI ratios. Under the circumstances of the analysis the calibration curve responded to the following equation:

Si/Al in framework=2.1008Si²⁺/A²⁺ by SIMS

By means of a profilometer the erosion velocity had been measured and corresponded to 0.17 nm/second.

COMPARATIVE EXAMPLE 1

An MFI aluminosilicate, in particular a ZSM-5, with a Si/Al ratio of about 89 was prepared by mixing solutions A and B.

Solution A: 9.1 g of sodium hydroxide in 25 ml of distilled water and 1.875 g of Al₂(SO₄)₃.18H₂O.

Solution B: 26.81 g of tetrapropylammonium bromide in 500 ml of distilled water and 108.18 g of colloidal silica containing 40 wt % Si02 (sold under the trade name of Ludox HS-40 and available in commerce from DuPont Chemicals).

200.26 gram of Solution B was mixed in a 300 ml autoclave for a period of 15 minutes and a hydrogel was obtained by adding slowly 12.11 gram of solution A. The pH of the aqueous solution was about 12.2. After stirring for 30 minutes at room temperature, the autoclave was fixed on a rotating axe of a laboratory oven. The crystallisation temperature was increased in about 2 hours to 150° C., which was maintained for 24 hours at a rotating speed of about 8 rpm. When synthesising the ZSM-5 the mixture had a constant H₂O/SiO₂ ratio of about 45 molar.

The product was cooled and washed with 10 litres of distilled water, dried at 110° C. for 16 hours and then calcined at 600° C. for 10 hours in order to remove the organic material.

The crystallinity of the obtained aluminosilicate was 100% and corresponded to the diffraction pattern of MFI zeolites. The crystals had a size of about 1.5-3 micrometer. The Si/Al profile as obtained by SIMS is given in FIG. 1.

COMPARATIVE EXAMPLE 2

An MFI aluminosilicate, in particular a ZSM-5, with a Si/Al ratio of about 60 was prepared by mixing solutions A and B.

Solution A: 46.47 g of sodium hydroxide in 50 ml of distilled water and 14.76 g of Al₂(SO₄)₃.16H₂O.

Solution B: 138.05 g of tetrapropylammonium bromide in 1020.2 ml of distilled water and 557.34 g of colloidal silica containing 40 wt % Si02 (Ludox HS-40).

Solutions B is put and mixed in a 2-litre autoclave for a period of 15 minutes and a hydrogel was obtained by adding slowly solution A. About 18 grams of sulphuric acid is added to reduce the pH down to 12.8. After stirring for 30 minutes at room temperature, the crystallisation reaction was performed at 150° C. for 24 hours in a stainless steel autoclave at a stirring rate of about 150 rpm. When synthesising the ZSM-5 the mixture had a constant H₂O/SiO₂ ratio of about 21 molar.

The product was cooled and washed with 10 litres of distilled water, dried at 110° C. for 16 hours and then calcined at 600° C. for 10 hours in order to remove the organic material.

The crystallinity of the obtained aluminosilicate was 100% and corresponded to the diffraction pattern of MFI zeolites. The crystals had a size of about 1-2 micrometer. The Si/Al profile as obtained by SIMS is given in FIG. 2.

EXAMPLE 1

An MFI aluminosilicate with a Si/Al ratio of about 90 was prepared by mixing solutions A and B.

Solution A: 27.6 g of sodium hydroxide in 27.6 ml of distilled water and 3.5 g of Al₂(SO₄)₃.16H₂O.

Solution B: 39.9 g of tetrapropylammonium bromide in 500 ml of distilled water and 161.3 g of colloidal silica containing 40 wt % Si02 (Ludox HS-40).

Solutions B is put and mixed in a 2-litre autoclave for a period of 15 minutes and a hydrogel was obtained by adding slowly solution A. The pH of the aqueous solution was about 12.5. After stirring for 30 minutes at room temperature, the crystallisation temperature was increased in about 2 hours to 150° C., which was maintained for 24 hours at a stirring rate of about 150 rpm. During crystallisation the aqueous solution in the autoclave was maintained under autogenous conditions—in other words the autoclave formed a closed reaction system at elevated temperature and pressure and the water content in particular was kept constant in the closed autoclave.

After an initial crystallisation period of 24 hours, with the aid of a valve, a leak was established in order to vaporise water as steam out of the reactor. Such vaporisation continued during a second subsequent crystallisation period of about 3 hours. During the second crystallisation period, the temperature and stirring rate were maintained. After 3 hours a total of 222 grams of water was recovered. During this vaporisation process the water/SiO₂ molar ratio in the synthesis mixture decreased from an initial value (during the initial crystallisation stage and at the commencement of the second crystallisation stage) of about 32 to a final value (at the end of the second crystallisation stage) of about 21.

The product was cooled and washed with 10 litres of distilled water, dried at 110° C. for 16 hours and then calcined at 600° C. for 10 hours in order to remove the organic material.

The crystallinity of the obtained aluminosilicate was 100% and corresponded to the diffraction pattern of MFI zeolites. The crystals had a size of about 1-2 micrometer. The Si/Al profile as obtained by SIMS is given in FIG. 3.

Table 1 provides a summary table with the relative molar compositions of the synthesis mixtures. When synthesising ZSM-5 corresponding to a mixture having a H₂O/SiO₂ ratio of about 21 molar (Comparative Example 2), no significant variation in the Si/Al profile is obtained. The same has been observed with a more diluted synthesis mixture, having a ratio of about 45 molar (Comparative Example 1). However, when during the synthesis after about 24 hours, the H₂O/SiO₂ ratio is changed from about 32 to about 21 (Example 1), a significant variation in the Si/Al profile is observed—the Si/Al atomic ratio was about 160 in the outer surface layer (about 10 nm thick) of the crystallites and decreased rapidly to a substantially constant bulk value (in an inner part of the crystallite extending inwardly from a depth from the surface of about 50 nm) of about 60. This change of concentration during the synthesis process has, to the inventor's knowledge, never been identified before. It is evident for the persons skilled in the art that modifications of the time and initial and final H₂O/SiO₂ ratios can be optimised in order to obtain desired surface and inner Si/Al ratios.

TABLE 1 Relative molar composition of synthesis mixture H₂O at H₂O Examples SiO₂ Al₂O₃ TPABr Na₂O start at end Comparative 1 0.00449 0.1392 0.1814 45.6 45.6 Example 1 Comparative 1 0.00629 0.1392 0.1694 21.0 21.0 Example 2 Example 1 1 0.00521 0.1390 0.1688 32.3 20.8 

1. A process for producing a crystalline metallosilicate composition, the method comprising the steps of: — a. providing an aqueous liquid phase comprising at least one silicon-containing compound and at least one metal-containing compound; and b. crystallising the crystalline metallosilicate composition from the aqueous liquid phase, the crystallising step having a first stage followed by a second stage and wherein the concentration of the at least one silicon-containing compound in the aqueous liquid phase is increased in the second stage.
 2. A process according to claim 1 wherein in the second stage the concentration of the at least one silicon-containing compound in the aqueous liquid phase is increased by removing water from the aqueous liquid phase.
 3. A process according to claim 2 wherein the crystallising step is carried out in a closed reaction vessel under elevated temperature and water is removed by permitting steam to be released from the reaction vessel.
 4. A process according to claim 3 wherein the elevated temperature is from 80 to 250° C.
 5. A process according to any one of claims 3 or 4 wherein the steam is progressively released over the second stage.
 6. A process according to any one of claims 3 or 4 wherein the steam is released at the commencement of the second stage.
 7. A process according to any one of claims 1 to 6 wherein at the commencement of the second stage the molar ratio of water to the at least one silicon-containing compound is from 60 to
 15. 8. A process according to any one of claims 1 to 7 wherein at the termination of the second stage the molar ratio of water to the at least one silicon-containing compound is from 54 to 7.5.
 9. A process according to any one of claims 1 to 8 wherein during the second stage the molar ratio of water to the at least one silicon-containing compound decreases by from 10 to 75%.
 10. A process according to any foregoing claim wherein the at least one silicon-containing compound is selected from at least one of an alkali metal silicate, a tetraalkyl orthosilicate, precipitated silica, pyrogenic silica, and an aqueous colloidal suspension of silica.
 11. A process according to any foregoing claim wherein the at least one metal-containing compound is selected from at least one of the metal oxide, a metal salt, and a metal alkoxide.
 12. A process according to claim 11 wherein the metallosilicate is an aluminosilicate, and the at least one metal-containing compound comprises an aluminium compound for which the source of aluminum is selected from at least one of hydrated alumina dissolved in an alkaline solution, aluminum metal, a water-soluble aluminum salt, such as aluminum sulphate or aluminium chloride, sodium aluminate and an alkoxide, such as aluminum isopropoxide
 13. A process according to claim 11 wherein the metallosilicate is a borosilicate, and the at least one metal-containing compound comprises a boron compound for which the source of boron is selected from at least one of hydrated boron oxide dissolved in an alkaline solution, a water-soluble boron salt, such as boron chloride, and an alkoxide.
 14. A process according to claim 11 wherein the metallosilicate is a ferrosilicate, and the at least one metal-containing compound comprises an iron compound for which the source of iron is a water soluble iron salt.
 15. A process according to claim 11 wherein the metallosilicate is a gallosilicate, and the at least one metal-containing compound comprises a gallium compound for which the source of gallium is a water soluble gallium salt.
 16. A process according to claim 11 wherein the metallosilicate is a titanosilicate, and the at least one metal-containing compound comprises a titanium compound for which the source of titanium is selected from at least one of titanium halides, titanium oxyhalides, titanium sulphates and titanium alkoxides.
 17. A process for producing a crystalline metallosilicate composition, the method comprising the steps of: — (a) providing an aqueous liquid comprising at least one silicon-containing compound dissolved or dispersed therein and at least one metal-containing compound dissolved or dispersed therein; (b) crystallising the crystalline metallosilicate composition from the aqueous liquid medium in a vessel under autogenous conditions, wherein in at least an end phase of the crystallising step a portion of the water is removed from the vessel; and (c) isolating the crystallised product.
 18. A process according to claim 17 wherein the water is removed as vapour.
 19. A process according to claim 17 or claim 18 wherein the water removal causes the concentration of at least the at least one silicon-containing compound dissolved or dispersed in the aqueous liquid to be increased.
 20. A process according to any one of claims 17 to 19 wherein the at least one silicon-containing compound is selected from at least one of an alkali metal silicate, a tetraalkyl orthosilicate, precipitated silica, pyrogenic silica, and an aqueous colloidal suspension of silica.
 21. A process according to any one of claims 17 to 20 wherein the at least one metal-containing compound is selected from at least one of the metal oxide, a water-soluble metal salt, and a metal alkoxide.
 22. A process according to any one of claims 17 to 21 wherein the metallosilicate is an aluminosilicate, a borosilicate, a ferrosilicate, a gallosilicate, or a titanosilicate.
 23. A process according to any one of claims 17 to 22 wherein the aqueous liquid further comprises a structure directing agent for the metallosilicate comprising at least one organic or inorganic compound containing nitrogen, oxygen, sulphur or phosphorous.
 24. A crystalline metallosilicate composition comprising crystallites having a crystal outer surface layer having a depth of about 10 nm below the outer surface, and an inner part extending inwardly from a depth of about 50 nm below the outer surface, wherein the atomic ratio of silicon to metal in the metallosilicate composition is at least 1.75 times higher in the crystal outer surface layer as compared to that in the inner part.
 25. A crystalline metallosilicate composition according to claim 24 wherein the inner part has a silicon/metal atomic ratio of from 15 to 1000, and the crystal outer surface layer has a silicon/metal atomic ratio of from 22.5 to
 15000. 26. A crystalline metallosilicate composition according to claim 24 or claim 25 wherein the inner part has a substantially constant silicon/metal atomic ratio.
 27. A crystalline metallosilicate composition according to any one of claims 24 to 26 wherein in the inner part the silicon/metal atomic ratio in the walls, constituting the pores in the crystalline metallosilicate composition, is substantially the same as the average silicon/metal atomic ratio of the inner part.
 28. A crystalline metallosilicate composition according to any one of claims 24 to 27 wherein the metallosilicate is an aluminosilicate, a borosilicate, a ferrosilicate, a gallosilicate, or a titanosilicate